CP33

Naidich Yu.V., Gab I.I., Kostyuk B.D., Stetsyuk T.V., Kurkova D.I., Dukarov S.V., Kryshtal A.P., Lytvyn O.S.
Processes of coagulation of metal nanofilms deposited on non-metallic materials.

Найдич Ю.В., Габ И.И., Костюк Б.Д., Стецюк Т.В., Куркова Д.И., Дукаров С.В., Крышталь А.П., Литвин О.С.
Процессы коагуляции металлических нанопленок, нанесенных на неметаллические материалы.

Ukraine / Украина

Processes of Ag, Mo, Cr, Ni, Nb, Ti, Pd, Pt, Rh nanofilms by thickness up to 100 nm coated oxide ceramics (Al2O3 and ZrO2) and carbon containing materials (ceramics on the basis of SiC, glass carbon) and annealed at 700–1600 °C coagulation are investigated. It is revealed, that change of morphology metallic nanofilms depends on system metal–nonmetal, temperatures and annealing environments, that results as in its division into separate fragments and coagulation in separate drops.

Исследованы процессы коагуляции нанопленок Ag, Mo, Cr, Ni, Nb, Ti, Pd, Pt, Rh толщиной до 100 нм, нанесенных на оксидную керамику (Al2O3 and ZrO2) и углеродсодержащие материалы (керамику на основе SiC, стеклоуглерод) и отожженных при 700—1600 °С. Установлено, что изменение морфологии металлических нанопленок зависит от системы металл—неметалл, температуры и среды отжига, что приводит как к разделению ее на отдельные фрагменты, так и к коагулированию в отдельные капли.